Fly-Ash Evaluation as Potential EOL Material Replacement of Cement in Pastes: Morpho-Structural and Physico-Chemical Properties Assessment.

The main objective of the study was to produce alternative binder materials, obtained with low cost, low energy consumption, and low CO2 production, by regenerating end-of-life (EOL) materials from mineral deposits, to replace ordinary Portland cement (OPC). The materials analyzed were ash and slag from the Turceni thermal power plant deposit, Romania. These were initially examined for morphology, mineralogical composition, elemental composition, degree of crystallinity, and heating behavior, to determine their ability to be used as a potential source of supplementary cementitious materials (SCM) and to establish the activation and transformation temperature in the SCM. The in-situ pozzolanic behavior of commercial cement, as well as cement mixtures with different percentages of ash addition, were further observed. The mechanical resistance, water absorption, sorptivity capacity, resistance to alkali reactions (ASR), corrosion resistance, and resistance to reaction with sulfates were evaluated in this study using low-vacuum scanning electron microscopy.

End-of-Life Materials Used as Supplementary Cementitious Materials in the Concrete Industry.

A sustainable solution for the global construction industry can be partial substitution of Ordinary Portland Cement (OPC) by use of supplementary cementitious materials (SCMs) sourced from industrial end-of-life (EOL) products that contain calcareous, siliceous and aluminous materials. Candidate EOL materials include fly ash (FA), silica fume (SF), natural pozzolanic materials like sugarcane bagasse ash (SBA), palm oil fuel ash (POFA), rice husk ash (RHA), mine tailings, marble dust, construction and demolition debris (CDD). Studies have revealed these materials to be cementitious and/or pozzolanic in nature. Their use as SCMs would decrease the amount of cement used in the production of concrete, decreasing carbon emissions associated with cement production. In addition to cement substitution, EOL products as SCMs have also served as coarse and also fine aggregates in the production of eco-friendly concretes.

Efficacy of Photon-induced Photoacoustic Streaming in the Reduction of Enterococcus faecalis within the Root Canal: Different Settings and Different Sodium Hypochlorite Concentrations.

INTRODUCTION: The purpose of this study was to determine the effectiveness of laser-activated irrigation by photon-induced photoacoustic streaming (PIPS) in the reduction of Enterococcus faecalis in root canal disinfection, varying laser energy output, and sodium hypochlorite (NaOCl) concentration. For effective removal of the smear layer, the sequence and resting time of the final irrigation steps were modified compared with the standard PIPS protocol. METHODS: Eighty-six extracted single-rooted teeth were mechanically prepared, sterilized, and inoculated with E. faecalis for 4 weeks. Teeth were divided into 9 groups and treated with an Er:YAG laser using a PIPS 600/9 tip at the following parameters: 10 mJ or 20 mJ, 15 Hz, and a 50-microsecond pulse duration at 0.15 W or 0.3 W average power, respectively. Root canals were irrigated with different concentrations of NaOCl (ie, 1%, 3%, and 5% and activated using the adjusted PIPS protocol). The bacterial count was performed immediately after and 48 hours after decontamination and new incubation on an agar plate. RESULTS: A statistically significant difference in bacterial counts (P < .05) was detected in all groups before and directly after the treatment and in groups treated with 5% NaOCl 48 hours after treatment. Scanning electron microscopic imaging showed an absence of bacteria and biofilm in the scanned areas after treatment with 5% NaOCl. CONCLUSIONS: Laser-activated irrigation using 5% NaOCl and a modified PIPS protocol resulted in effective eradication of the bacterial biofilm and removal of the smear layer.